I assume you are using a hardened steel nozzle. But still, I am wondering if the repeated friction between copper and steel would damage the steel also. A lot slower than a regular nozzle, but it’s like a thousand needle pricks as I understand it. How is your nozzle holding up?
I assume you are using a hardened steel nozzle. But still, I am wondering if the repeated friction between copper and steel would damage the steel also. A lot slower than a regular nozzle, but it’s like a thousand needle pricks as I understand it. How is your nozzle holding up?
Pretty well. It’s the Bambu hardened steel nozzle so it should be able to stand it.